FRPE-70P

2022-06-21

Specification

This product can effectively improve the oxygen index , the char formation ,Anti - drop performance，and smoke suppression ability of polyolefin material.
There is no obvious negative effect on the mechanical properties of the material, the tensile strength and elongation can be improved with the appropriate conditions.
It can be used as synegetic flame retardants with halogen-free flame retardants such as magnesium hydroxide, aluminum hydroxide, calcium carbonate,etc.
Improve the surface smoothness of extruded products, improve the processing performance.
It is non-toxic and environment-friendly, and conforms with EU ROHS directive and REACH regulations.

Application

This product is mainly used in flame retardant materials of various organic polymer systems, especially suitable for environmentally friendly flame retardant formulation systems of polyolefin materials.

Physical Characteristics

Item	Unit	FRPE-70P	Test Method
Appearance	/	灰白色	/
Diameter	mm	3～4	/
Length	mm	3~8	/
Density	g/cm3	1.43±0.02	ASTM D792-2007

SEM Image

Application data

materiel apellation		blank group	Example1	Example2	Example3	Example4
LDPE		50.0	48.0	47.0	46.0	45.0
compatilizer		5.0	4.8	4.7	4.6	4.5
processing aid		2.0	1.9	1.9	1.8	1.8
PE wax		1.0	1.0	0.9	0.9	0.9
hydroxid		42.0	40.3	39.5	38.6	37.8
FRPE-70		/	4.0	6.0	8.0	10.0
performance
density	g/cm3	1.23	1.24	1.25	1.26	1.27
oxygen index	%	28.0	29.5	30.0	31.5	30.5
tensile strength	MPa	17.6	20.1	21.0	21.0	19.6
elongation at break	%	504.0	460.0	504.0	550.0	484.0

Note:In this experiment, the mixing temperature is 170 ℃ .The recommended addition amount in polyolefin cable material is 8%

Typical test data are listed in the above Tables unless otherwise specified.

Low-smoke halogen-free flame retardant materials

FRPE-70P